Product Data Sheet Show all documents

SikaPower®-1200

Fast curing, tough and high strength assembly adhesive

SikaPower®-1200 is a tough, high strength, solvent free, thixotropic, fast curing epoxy adhesive. It is designed for fast assembly bonding of structural composite substrates, like GFRP and CFRP laminates, as well as metallic substrates. The adhesive cures by polyaddition of the two components.  

  • High fatigue and impact resistance
  • Long open time at high temperature and humidity
  • Cures at room temperature
  • Accelerated curing and higher mechanical strength with heat
  • Good adhesion to fiber-reinforced plastics
  • Does not contain solvents or PVC
 
Product Data Sheet Show all documents

PRODUCT BENEFITS

  • High fatigue and impact resistance
  • Long open time at high temperature and humidity
  • Cures at room temperature
  • Accelerated curing and higher mechanical strength with heat
  • Good adhesion to fiber-reinforced plastics
  • Does not contain solvents or PVC

 

Usage

SikaPower®-1200 is suitable for fast assembly bonding of highly stressed components, especially if high strength and high fatigue properties are required.
This product is suitable for professional experienced users only. Tests with actual substrates and conditions have to be performed ensuring adhesion and material compatibility.  

Packaging

SikaPower®-1200 (A)

Drum

220 kg

SikaPower®-1040 (B)

Drum

240 kg

SikaPower®-1200 (A+B)

Cartridge

400 ml

Mixer: Sulzer MixPacTM MFH 10-24T

Cartridge

450 ml

Mixer: Sulzer MixPacTM MGQ 08-24T

 

Product Details

Typical Product Data
Properties

Component A

SikaPower®-1200

Component B

SikaPower®-1040

Chemical Base

Epoxy

Amine

Color (CQP001-1)

  

mixed

 

Yellow

Blue

Green

Density

  

mixed, calculated

1.15 g/cm3

1.25 g/cm3

1.18 g/cm3

Mixing Ratio

A:B by volume

A:B by weight

100:50

100:54

Solid Content

100 %

Viscosity (CQP029-4)

at 10 s-1

120 Pa·s A

45 Pa·s A

Consistency

Thixotropic paste

Application Temperature

15 ─ 30 °C

Open time (CQP046-11 / ISO 4587)

45 min B, C, D

Curing time (CQP046-9, ISO4587)

at 23 °C

at 70 °C

48 hours

2 hours

Tensile Strength (CQP543-1 / ISO 527)

40 MPa C, E

E-Modulus (CQP543-1 / ISO 527)

2600 MPa C, E

Elongation at Break (CQP543-1 / ISO 527)

3.5 % C, E

Tensile Lap-Shear Strength (CQP046-9 / ISO 4587)

20 MPa C, D, E

Critical Stress Intensity Factor KIc (ISO 13586)

2.7 m1/2 MPa C, E, F

Critical Energy Release Rate GIc (ISO 13586)

3.5 N/mm C, E, F

Glass Transition Temperature (CQP509-1 / ISO 6721)

90 °C E

Shelf Life

12 months G

CQP = Corporate Quality Procedure

A) Rheometer PP = 25, d = 1 mm

B) cured for 7 days at 23 °C

C) 23 °C / 50 % r. h.D) adhesive layer: 25 x 10 x 3 mm / on GFRPE)  cured for 4 hours at 70 °C
F) CT-specimens (Optical Crack Tracking)G) stored between 10 and 35 °C
Technical Information

CURE MECHANISM

SikaPower®-1200 cures by chemical reaction of the two components at room temperature. Higher temperatures speed up the curing process and lower temperatures slow down the curing process. The final glass transition temperature, as well as the tensile and shear strengths, may be increased with higher curing temperature.

CHEMICAL RESISTANCE

In view of potential chemical or thermal exposure, it is required to conduct a project related testing.

Application

Application Information

Surface Preparation

SikaPower®-1200 adheres usually well to fiber-reinforced plastics if applied subsequently after the removal of the protective peel ply.

Surfaces must be clean, dry and free from grease, oil and dust. Surface treatment may be required depending on the specific nature of the substrates. All pre-treatment steps must be confirmed by preliminary tests on original substrates considering specific conditions in the assembly process.

Application

SikaPower®-1200 is dispensed from dual cartridges with adequate manual or pneumatic guns. Extrude adhesive without mixer to equalize the filling levels. Attach the mixer and dispose of the first few cm of the bead before the application.

For advice on selecting and setting up a suitable pump system, contact the System Engineering Department of Sika Industry.

 

Removal

Uncured SikaPower®-1200 may be removed from tools and equipment with Sika® Remover-208 or another suitable solvent. Once cured, the material can only be removed mechanically.
Hands and exposed skin have to be washed immediately using hand wipes such as Sika® Cleaner-350H cleaning towels or a suitable industrial hand cleaner and water.

Do not use solvents on skin.

STORAGE CONDITIONS

SikaPower®-1200 has to be stored between 10 °C and 35 °C in a dry place. Do not expose to direct sunlight of frost. After opening of the packaging, the contents have to be protected against humidity.

Documents