Sikafloor® Marine-530

IMO approved self-levelling, 2-component polyurethane decorative resin

Sikafloor® Marine-530 is a 2-component, polyurethane, elastic, low VOC self-smoothing marine flooring resin. It is part of the Sikafloor® Marine decorative resin systems. Sikafloor® Marine-530 has been tested according to FTP Code system and approved according the IMO Marine Equipment Directives.  

  • Good application characteristics
  • Very low VOC emission
  • IMO Approved
  • Solvent-free
  • Longterm elastic
  • Good mechanical resistance
  • IMO approved, as floor covering up to a max. of 2.6 kg/m2
 
Product Data Sheet Show all documents

PRODUCT BENEFITS

  • Good application characteristics
  • Very low VOC emission
  • IMO Approved
  • Solvent-free
  • Longterm elastic
  • Good mechanical resistance
  • IMO approved, as floor covering up to a max. of 2.6 kg/m2
 

Usage

Sikafloor® Marine-530 can be used  interior as wearing layer levelling compound in ship and boat construction. For interior comfort floor solution and exterior as a black deck caulking in the Sikafloor® Marine Deco Teak solutions. This product is suitable for experienced professional users only. Tests with actual substrates and conditions have to be performed ensuring adhesion and material compatibility.  

Packaging

Sikafloor® Marine-530 (A)

Container

15.8 kg

Sikafloor® Marine-530 (B)

Container

4.2 kg

Product Details

Typical Product Data
Properties

Sikafloor® Marine-530 (A)

Sikafloor® Marine-530 (B)

Chemical Base

Polyurethane

Isocyanate

Color (CQP001-1)

mixed

Coloured

Yellowish

Various colours available (see color design chart)

Density

mixed

1.2 kg/l

1.2 kg/l

1.2 kg/l

Solid Content

100 %

Mixing Ratio

by weight

79 : 21

Application Temperature

substrate / climate

10 ─ 30 °C A, B

Working Time

10 °C

20 °C

30 °C

21 minutes

15 minutes

12 minutes

Shore A Hardness (CQP023-1 / ISO 48-4)

83

Tensile Strength (DIN 53504)

8 MPa

Elongation at Break (DIN 53504)

180 %

Shelf Life

9 months C

12 months C

CQP = Corporate Quality Procedure

A) Substrates must be 3 °C above the dew point

B) max. 80 % r.h.C) stored in sealed container in up-right position in a dry place between 5 and 30 °C, protected from direct sunlight
Technical Information

CURE MECHANISM

The curing of Sikafloor® Marine-530 takes place by a chemical reaction of the two components.
Higher temperatures speed up and lower temperatures slow down the curing process.

CHEMICAL RESISTANCE

For advice contact the Technical Department of Sika Industry.

Application

Application Information

Surface Preparation

In the case of cementitious substrates, it must be ensured that the laitance layer is completely removed. This is usually achieved by grinding. All dust, loose and friable material must be completely removed by vacuum before the next application.
Repairs to the substrate, filling of cracks, holes/voids or surface levelling must be carried out first. Repair areas must be cured before applying primers.
Ensure the substrate moisture content is equal or less than 4 % (Calcium carbide method (CM-method). Apply Sikafloor®-150/-151 as a primer to obtain a closed pore free surface.
2-C polyurethane substrates need usually to be sanded with 40 – 80 grit sanding paper up to diamond disc. In case the substrate is not clean, it is required to clean it before the sanding process to ensure no debris is sanded into the surface. All dust, loose and friable material must be completely removed from the surface by vacuum cleaning before next application.
For more information and other substrates refer to the Sika Pre-Treatment Chart for Sikafloor® Marine Applications.
The application area must be protected against dirt, sun light, water and draught.

Application

Sikafloor® Marine-530 is poured and spread evenly by means of a suitable trowel or pin leveller. A spike roller may be used to improve levelling and de-airing.
For liquid application on cambers and slopes multiple applications steps might be needed.
A seamless finish can be achieved when a “wet” edge is maintained during application.

 

Curing

Indications regarding curing details see table below.

Tempera-
ture

Walk- and overcoatable

Full loading

10 °C

36 hours

7 days

20 °C

24 hours

7 days

30 °C

16 hours

7 days

Removal

Uncured Sikafloor® Marine-530 can be removed from tools and equipment with Sika® Colma Cleaner or another suitable solvent. Once cured, the material can only be removed mechanically.
Hands and exposed skin have to be washed immediately using hand wipes such as Sika® Cleaner-350H or a suitable industrial hand cleaner and water.

Do not use solvents on skin.

Application Limits

Beware of condensation. The substrate and uncured applied product must be at least 3 °C above dew point to reduce the risk of condensation.
Freshly applied Sikafloor® Marine-530 must be protected from damp, condensation and water for at least 1 day. Uncured material reacts in contact with water (foaming).
For consistent color matching, ensure the product in each area is applied from the same batch numbers.
For air heating use only electric powered warm air blower systems.
If Sikafloor® Marine-530 is used in interior areas and exposed to UV light, the floor must be protected by a pigmented sealer, such as Sikafloor® Marine-505.

STORAGE CONDITIONS

The product must be stored in original, unopened and undamaged packaging in dry conditions at temperatures between +5 °C and
+30 °C. Always refer to packaging.

After opening of the packaging, the contents need to be protected against moisture. 

Documents