Sikafloor® MultiDur ES-25 ESD
Sikafloor® MultiDur ES-25 ESD is a tough elastic, decorative and protective dissipative self-smoothing flooring system for concrete or cement screeds with normal up to medium heavy wear.
Particularly suitable for areas with requirements for a low electrostatic charge and dissipative surface.
- Body voltage generation < 30 V*
- Good mechanical and chemical resistance
- Easy application & easy to clean
- Tough elastic
- Conforms to the requirements of ANSI/ESD S20.20 and IEC 61340-5-1
- Low VOC and particle emission
- Fulfils ESD-requirements at > 25 % RH/+23 °C**
Usage
It is used as: Dissipative coloured indoor system for electrostatic protected areas (EPA). Typical applications include industries that want to reduce ESD events and assemble, install, test or transport electrostatic sensitive devices such as:- Semiconductors and clean rooms
- Pharmaceutical industries
- Automotive industries
Advantages
- Body voltage generation < 30 V*
- Good mechanical and chemical resistance
- Easy application & easy to clean
- Tough elastic
- Conforms to the requirements of ANSI/ESD S20.20 and IEC 61340-5-1
- Low VOC and particle emission
- Fulfils ESD-requirements at > 25 % RH/+23 °C**
Packaging
Please refer to individual Product Data Sheet.
Colour
Almost unlimited choice of colour shades.
Due to the nature of carbon fibres providing the conductivity, it is not possible to achieve exact colour matching. With very bright colours (such as yellow and orange), this effect is increased. Under direct sunlight there may be some variations and colour variation, this has no influence on the function and performance of the coating.
Appearance
Self-smoothing system – semi-gloss finish
System Details
APPROVALS / STANDARDS
- *Testing of electrostatic properties in accordance to IEC 61340-5-1, Polymer Institute, Test Report P 4956-1-E, November 2007
- **Testing of electrostatic properties in accordance to IEC 61340-5-1, SP Institute, Test Report F900355:B, February 2009
- Fire classification in accordance with EN 13501-1, Report-No. 2007-B-0181/18, MPA Dresden, Germany, May 2007
- Particle emission certificate Sikafloor-235 ESD CSM Statement of Qualification - ISO 14644-1, class 4 - Report No. SI 0706-406 and GMP class A, Report No. SI1008-533.
- Outgassing emission certificate Sikafloor-235 ESD: CSM Statement of Qualification - ISO 14644-8, class -6.8 - Report No. SI 0706-406.
- Biological Resistance in accordance with ISO 846, CSM Report No. SI 1008-533.
- Testing of Paint Compatibility in acc. to BMW-Standard 09-09-132-5, Polymer Institute, Test Report P 5541, August 2008
- Varnishability test according to Mercedes Benz-standard PBODC380/PBVCE380 (paint wetting impairment substances (PWIS)) like silicones, Test Report VPT-Nr. 07LL165, 04.2008
- Spark resistance in accordance with UFGS-09 97 23 of coating systems, Test report P 8625-E, Kiwa Polymer Institut, March 2014
System Structure
Sikafloor® MultiDur ES-25 ESD:
1. Primer + Earthing connection | Sikafloor®-161 HC + Sika® Earthing Kit |
2. Conductive primer | Sikafloor®-220 W Conductive |
3. Final ESD coating | Sikafloor®-235 ESD filled with Sikafloor® Filler 1 |
Note: Alternatively quartz sand F34* can be used as a filler, which will result in a gloss finish with a slight change of the aesthetical appearance.
The system configuration as described must be fully complied with and may not be changed.
Composition
Epoxy
Nominal Thickness
~ 1.0 - 1.5 mm
Volatile organic compound (VOC) content
Very low content of volatile organic compounds. Sikafloor®-235 ESD, the finishing layer of the Sikafloor® MultiDur ES-25 ESD System has been awarded the Frauenhofer IPA CSM Certicate of Qualification with the report number SI 0706-406. The outgassing test was performed in accordance with CSM procedures. TVOC: ISO-AMC Class -6.8 (see ISO 14644-8).
Shelf Life
Please refer to individual Product Data Sheet.
Storage Conditions
Please refer to individual Product Data Sheet.
Shore D Hardness
~ 58 (resin filled) | (7 days / +23 °C) |
Abrasion Resistance
~ 60 mg (CS 10/1000/1000) | (28 days / +23 °C) |
Compressive Strength
~ 44 N/mm² (resin filled) | (28 days / +23 °C) |
Tensile Strength
~ 20 N/mm² (resin filled) | (28 days / +23 °C) |
Reaction to Fire
Cfl-s1 | (EN 13501-1) |
Chemical Resistance
Resistant to many chemicals. Contact Sika technical service for specific information.
Temperature Resistance
Exposure* | Dry heat |
Permanent | +50 °C |
Short-term max. 7 d | +80 °C |
*No simultaneous chemical and mechanical exposure.
USGBC LEED Rating
Conforms to the requirements of LEED EQ Credit 4.2: Low-Emitting Materials: Paints & Coatings SCAQMD Method 304-91 VOC Content < 100 g/l
Electrostatic Behaviour
Resistance to ground1 | Rg < 109 Ω | (IEC 61340-4-1) |
Typical average resistance to ground2 | Rg < 106 Ω | (DIN EN 1081) |
Body voltage generation2 | < 100 V | (IEC 61340-4-5) |
System Resistance (Person/Floor/Shoe)3 | < 35 M Ω | (IEC 61340-4-5) |
1 In accordance with IEC 61340-5-1 and ANSI/ESD S20.20.
2 Readings may vary, depending on ambient conditions (i.e. temperature, humidity) and measurement equipment.
3 Or < 109 Ω + body voltage generation of < 100 V, in case of readings > 35 M Ω.
Application
Ambient Air Temperature
+10 °C min. / +30 °C max.
Relative Air Humidity
80 % r.h. max.
Dew Point
Beware of condensation!
The substrate and uncured floor must be at least 3 °C above dew point to
reduce the risk of condensation or blooming on the floor finish.
Substrate Temperature
+10 °C min. / +30 °C max.
Substrate Moisture Content
<4 % pbw moisture content.
Test method: Sika Tramex Meter, CM-measurement or Oven-Dry-Method.
No rising moisture according to ASTM (Polyethylene-sheet).
Waiting Time / Overcoating
Before applying Sikafloor®-220 W Conductive on Sikafloor®-161 HC allow:
Substrate temperature | Minimum | Maximum |
+10°C | 24 hours | 4 days |
+20°C | 12 hours | 2 days |
+30°C | 8 hours | 1 days |
Before applying Sikafloor®-235 ESD on Sikafloor®-220 W Conductive allow:
Substrate temperature | Minimum | Maximum |
+10°C | 26 hours | 7 days |
+20°C | 17 hours | 5 days |
+30°C | 12 hours | 4 days |
Times are approximate and will be affected by changing ambient conditions particularly temperature and relative humidity.
Applied Product Ready for Use
Temperature | Foot traffic | Light traffic | Full cure |
+10°C | ~ 4 days | ~ 8 days | ~ 10 days |
+20°C | ~ 3 days | ~ 6 days | ~ 7 days |
+30°C | ~ 2 days | ~ 5 days | ~ 6 days |
Note: Times are approximate and will be affected by changing ambient conditions
Consumption
Coating | Product | Consumption |
Primer | Sikafloor®-161 HC | 1-2 x ~ 0.3 - 0.5 kg/m² |
Levelling (if required) | Sikafloor®-161 HC levelling mortar | Refer to PDS of Sikafloor®-161 HC |
Earthing connection | Sika® Earthing Kit | 1 earthing point per approx. 200 -300 m², min. 2 per room. |
Conductive Primer | Sikafloor®-220 W Conductive | 1 x 0.08 - 0.10 kg/m² |
Final ESD Coating, film thickness ~1.0 mm | Sikafloor®-235 ESD filled with Sikafloor® Filler 1* | Maximum 1.6 kg/m² Binder + Sikafloor® Filler 1. Filling grade: 1 : 0.1 pbw to 1 : 0.2 pbw (Depending on the air temperature the filling grade varies) |
Final ESD Coating, film thickness ~1.5 mm | Sikafloor®-235 ESD filled with quartz sand F34* | Maximum 2.5 kg/m² Binder + quartz sand F 34: 1 : 0.1 pbw to 1 : 0.3 pbw (Depending on the air temperature the filling grade varies) |
These figures are theoretical and do not allow for any additional material due to surface porosity, surface profile, variations in level or wastage etc.
*All values have been determined using quartz sand F 34 (0.1-0.3 mm) from Quarzwerke GmbH Frechen and Sikafloor® Filler 1. Other quartz sand type will have an effect on the product, such as filling grade, levelling properties and aesthetics. Generally, the lower the temperature the less the filling grade.
CLEANING
Please refer to the Sikafloor® Cleaning Regime.