SikaCor® VE MY
Vinylester Resin Based Laminate System
SikaCor® VE MY is 2 part, vinly-ester based coating and lining system.
- High chemical resistance to acids, leaches, solvents and to oxidising agents
- Applicable on concrete
- Fast curing
- Crack bridging properties as laminate layer
- Excellent bond strength
- Easy application
- For internal and external use
Usage
- Especially designed for the use in a chemically stressed environment, where a high chemical resistance is mandatory.
- Internal and external lining of chemical tanks
- Secondary containment lining in bund areas
- Binder for GFR laminate systems
- Lining of gutters in process and storage areas
Advantages
- High chemical resistance to acids, leaches, solvents and to oxidising agents
- Applicable on concrete
- Fast curing
- Crack bridging properties as laminate layer
- Excellent bond strength
- Easy application
- For internal and external use
Packaging
| Part A |
|
| Part B | 5 kg bottle |
Colour
| Part A (Solution) | Transparent liquid |
| Part B (Hardener) | Transparent liquid |
Product Details
Composition
Vinyl Ester
Shelf Life
3 months from date of production
Storage Conditions
Store properly in original, unopened and undamaged sealed packaging, in dry conditions at temperatures between +5 °C and +25 °C. Keep away from direct sunlight, rain and water.
Density
~1.05 kg/l
Tensile Strength in Flexure
| 150 MPa | (ASTM D 790) |
Tensile Strength
| 85 MPa | (ASTM D 638) |
Tensile Adhesion Strength
| > 1.5 N/mm² (failure in concrete) | (ISO 4624) |
Chemical Resistance
| Chemical | Concentration | Recommended maximum continuous exposure temperature |
| Hydrochloric Acid* | < 37 % | +38 °C |
| Sulphuric Acid | < 70 % | +82 °C |
| Nitric Acid | < 30 % | +38 °C |
| Hydrogen Peroxide | < 30 % | +27 °C |
| Chromic Acid | < 20 % | +49 °C |
| *Double C-glass veil required. Acid resistant (E-CR) glass recommended in chopped glass behind veil layers. Total thickness (veil + chopped glass + SikaCor® VE MY resin) should be ~5 mm (~0.200 inches thick) |
SikaCor® VE MY is resistant to a wide range of chemicals, please provide Sika with detailed aspects of application, usage and service.
Application
Mixing Ratio
Laminate layer and top coat
Part A : Part B = 100 : 1.0–2.0 (by weight)
Ambient Air Temperature
+5 °C min. / +35 °C max.
Relative Air Humidity
80 % r.h. max.
Dew Point
Beware of condensation!
The substrate and uncured floor must be at least +3 °C above the dew point to reduce the risk of condensation or blooming on the floor finish.
Substrate Temperature
+5 °C min. / +35 °C max.
Substrate Moisture Content
< 4 % pbw moisture content.
Test method: Sika® Tramex meter, CM - measurement or Oven-dry-method. No rising moisture according to ASTM D 4263 (Polyethylene-sheet).
Pot Life
~10 minutes (at +30 °C)
Curing Time
| Foot traffic | After 4 hours |
| Fully cured | After 2 days |
Note: Times are approximate and are effected by changing ambient conditions.
Waiting Time / Overcoating
| Substrate Temperature | Minimum | Maximum |
| +30 °C | ~2 hours | ~2 days |
Note: Times are approximate and are affected by changing ambient conditions
Consumption
SikaCor® VE MY System on concrete
| Primer | SikaCor® VE MY solution : SikaCor® VE MY hardener | 100 : 1–2 |
| Scratch coat for floors | SikaCor® VE MY solution : SikaCor® VE MY hardener : Sikadur®-504 | 100 : 1–2 : 80–100 |
| Scratch coat for walls | (SikaCor® VE MY solution : SikaCor® VE MY hardener) + Extender-T | (100 : 1–2) + 2–3 % Extender-T |
| SikaCor® VE MY resin for laminate layer, surface veil and top coat | SikaCor® VE MY solution : SikaCor® VE MY hardener | 100 : 1–2 |
Note: All ratios are by weight
Economical System
| Coating System | Product | Consumption |
| Primer | 1 coat × SikaCor® VE MY resin | ~0.20 kg/m² |
| Scratch coat for floors | 1–2 coats × SikaCor® VE MY resin + Sikadur®-504 (quartz sand) | 0.20–0.30 kg/m² |
| Scratch coat for walls | 1–2 coats × SikaCor® VE MY resin + Extender-T | 0.20–0.30 kg/m² |
| 1st laminate layer | SikaCor® VE MY resin + Sika® Reemat ECR CSM-300 | ~0.90 kg/m² |
| Surface veil | SikaCor® VE MY resin + Sika® Reemat SM30 | ~0.20 kg/m² |
| Top coat | 2 coats × SikaCor® VE MY resin | 0.15–0.20 kg/m²/coat |
Standard System
| Coating System | Product | Consumption |
| Primer | 1 coat × SikaCor® VE MY resin | ~0.20 kg/m² |
| Scratch coat for floors | 1–2 coats × SikaCor® VE MY resin + Sikadur®-504 (quartz sand) | 0.20–0.30 kg/m² |
| Scratch coat for walls | 1–2 coats × SikaCor® VE MY resin + Extender-T | 0.20–0.30 kg/m² |
| 1st laminate layer | SikaCor® VE MY resin + Sika® Reemat ECR CSM-300 | ~0.90 kg/m² |
| 2nd laminate layer | SikaCor® VE MY resin + Sika® Reemat ECR CSM-300 | ~0.90 kg/m² |
| 1st surface veil | SikaCor® VE MY resin + Sika® Reemat SM30 | ~0.20 kg/m² |
| 2nd surface veil | SikaCor® VE MY resin + Sika® Reemat SM30 | ~0.20 kg/m² |
| Top coat | 2 coats × SikaCor® VE MY resin | 0.15–0.20 kg/m²/coat |
Heavy Duty System
| Coating System | Product | Consumption |
| Primer | 1 coat × SikaCor® VE MY resin | ~0.20 kg/m² |
| Scratch coat for floors | 1–2 coats × SikaCor® VE MY resin + Sikadur®-504 (quartz sand) | 0.20–0.30 kg/m² |
| Scratch coat for walls | 1–2 coats × SikaCor® VE MY resin + Extender-T | 0.20–0.30 kg/m² |
| 1st laminate layer | SikaCor® VE MY resin + Sika® Reemat ECR CSM-450 | ~1.25 kg/m² |
| 2nd laminate layer | SikaCor® VE MY resin + Sika® Reemat ECR CSM-450 | ~1.25 kg/m² |
| 1st surface veil | SikaCor® VE MY resin + Sika® Reemat SM30 | ~0.20 kg/m² |
| 2nd surface veil | SikaCor® VE MY resin + Sika® Reemat SM30 | ~0.20 kg/m² |
| Top coat | 2 coats × SikaCor® VE MY resin | 0.15–0.20 kg/m²/coat |
The consumption stated above are estimates. For actual consumption, site trials are recommended. Please contact our Sika sales team for more information.
SUBSTRATE PREPARATION
Concrete substrates must be sound and of sufficient compressive strength (minimum 25 N/mm²) with a minimum pull-off strength of 1.5 N/mm².
The substrate must be clean, dry and free of all contaminants such as dirt, oil, grease, coatings, surface treatments, etc. If in doubt, apply a test area first.
Concrete substrates must be prepared mechanically using abrasive blast cleaning or grinding equipment to remove cement laitance and achieve an open textured surface.
Weak concrete must be removed and surface defects such as blowholes and voids must be fully exposed.
Repairs to the substrate, filling of blowholes/voids and surface levelling must be carried out using appropriate products from Sika® MonoTop® or SikaCor® VE MY screed.
The concrete or screed substrate has to be primed or levelled in order to achieve an even surface.
High spots must be removed by grinding.
All dust, loose and friable material must be completely removed from all surfaces before application of the product, preferably by brush and/or vacuum.
For more information, please refer to "Method Statement-Evaluation and Preparation of Concrete Surfaces for Sika's Flooring System (Doc. No. CA/006/21082018)
MIXING
Prior to mixing, stir part A mechanically. When all of part B has been added to part A, mix continuously for 1–2 minutes until a uniform mix has been achieved.
To ensure thorough mixing pour materials into another container and mix again to achieve a consistent mix.
Over mixing must be avoided to minimise air entrainment.
When adding Extender-T or Quartz Sand, mix these components with part A for ~1 minute before adding part B.
APPLICATION
Prior to application, confirm substrate moisture content, r.h. and dew point.
Primer
Apply 1 primer coat of SikaCor® VE MY using a roller and let it cure.
Scratch Coat
Rough surface need to be levelled first. Apply 1–2 layers of scratch coat by trowel to the required thickness and let it cure.
Laminate Layer
Apply the first layer of SikaCor® VE MY by roller, imbed the glass fabric. Apply the second and third layer in the same way, wet on wet. After application of the final glass fabric, de-aerate and wet out the glass fabric using a laminating or disk roller
Important Note: Ensure a min. 5 cm overlapping of the glass fabric.
Top Coat
Apply 2 coats of SikaCor® VE MY by roller.
Important Notes:
- During application a high air change rate has to be provided.
- Water, even in the smallest amount, could affect the hardening and block the curing process. Tools and equipment have to be totally dry.
- Appropriate eye protection shall be worn at all times while handling and mixing products.
- Approved respiratory protection masks (eg. Half face-piece reusable respirator 6200, respiratory protection with replaceable cartridges/filters from 3M) shall be worn at all times to protect the nose and mouth from inhaling fumes from the material.
- Safety shoes, rubber gloves and other appropriate skin protection shall be worn at all times.
CLEANING OF TOOLS
Clean all tools and application equipment with acetone immediately after use. Hardened and/or cured material can only be removed mechanically.
Attention: Acetone is a flammable liquid, please handle with care. The use of Personal Protection Equipment (PPE) is mandatory.