Sika® Injection-201 CE
Sika® Injection-201 CE is a very low viscous, elastic and solvent-free polyurethane injection resin. In contact with water, a uniform, closed and therefore watertight pore structure forms, which is elastic and flexible.
- Permanently elastic, can absorb limited movements
- No shrinkage in subsequent dry conditions
- Due to its low viscosity it can penetrate into cracks >0.2 mm in width
- Cured Sika® Injection-201 CE is inert and chemically-resistant
- Solvent-free
- In cold temperatures (< +10°C) Sika® Injection-201 CE can be accelerated using Sika® Injection-AC20
- Can be injected as a one component system
Usage
- Sika® Injection-201 CE is used for permanent watertight sealing with some flexibility to absorb limited movement, in dry, damp or water-bearing cracks and joints in concrete, brickwork and natural stone
- Sika® Injection-201 CE can be used for the injection of the SikaFuko®-System (non re-injectable!)
- For use in water-bearing cracks under hydrostatic pressure, preliminary injection shall be made with Sika® Injection-101 RC
Advantages
- Permanently elastic, can absorb limited movements
- No shrinkage in subsequent dry conditions
- Due to its low viscosity it can penetrate into cracks >0.2 mm in width
- Cured Sika® Injection-201 CE is inert and chemically-resistant
- Solvent-free
- In cold temperatures (< +10°C) Sika® Injection-201 CE can be accelerated using Sika® Injection-AC20
- Can be injected as a one component system
Packaging
Part A | 10 kg, 20 kg |
Part B | 10.6 kg, 21.2 kg |
Colour
Part A | colourless |
Part B | brown |
Product Details
APPROVALS / STANDARDS
- German KTW drinking water certificate
- Concrete injection for ductile filling of cracks, voids and interstices (D) according to EN 1504-5:2004, Declaration of Performance 35859175, certified by notified factory production control certification body 0761 and provided with the CE marking.
Composition
Water reactive 2-part polyurethane resin, solvent free
Shelf Life
36 months from date of production if stored properly in undamaged, unopened, original sealed packaging.
Storage Conditions
Dry storage at temperatures between +5 °C and +35 °C. Protect from direct sunlight and humidity.
Density
Part A | Part B |
~1.00 kg/l | ~1.07 kg/l |
All density values determined at +20 °C
Viscosity
~100 mPa·s (mixture, +20 °C) | (ISO 3219) |
Shore A Hardness
~43 (7 days) | (EN 868) |
Modulus of Elasticity in Flexure
~2 MPa | (ISO 527-1) |
Application
Mixing Ratio
Part A:Part B 1:1 parts by volume
Reaction time table Sika® Injection-201 CE
(ISO 9514)
Material Temperature | |||
Dosage* | +5 °C | +10 °C | +20 °C |
0.0 % | ~180 min | ~180 min | ~135 min |
0.5 % | ~60 min | ~55 min | ~38 min |
1.0 % | ~29 min | ~32 min | ~24 min |
2.0 % | ~16 min | ~17 min | ~13 min |
3.0 % | ~13 min | ~14 min | ~10 min |
5.0 % | ~9 min | ~7 min | ~5 min |
*Dosage of Sika® Injection-AC20 in % by weight of Sika® Injection-201 Comp. A
The given data are laboratory parameters and may deviate depending on the object and conditions on site.
Ambient Air Temperature
+5°C min. / +35°C max.
Substrate Temperature
+5°C min. / +35°C max.
SUBSTRATE PREPARATION
Surfaces of cavities and cracks need to be clean, free of loose particles, dust, oil and any other bond-breaking substances. Any dirt must be blown out by compressed air.
MIXING
Empty parts A and B into a mixing vessel and mix slowly and thoroughly for at least 3 min (max. 250 rpm) until homogeneous, observing the safety precautions. The containers are supplied according to the required mixing ratio of 1 : 1 parts by volume.
Partial quantities can be measured out into separate vessels.
After mixing, pour the material into the pump’s feed container, stir briefly and use within the pot life.
If the substrate and/or ambient temperatures are < +10°C, Sika® Injection-AC20 can be added to accelerate the reaction time.
CLEANING OF TOOLS
Clean all tools and application equipment according to the Product Data Sheet for the Sika®Injection Cleaning System
FAQ
1-component or 2-components PU injection foam/resin can be used to seal leakages on cracked concrete.
1-component PU injection foam
2-components PU injection foam / resin
For more information, please consult Sika’s Technical Service Department.
PU injection foam requires water to react. As it reacts, it will foam and expand to stop the water leaks within a short period. PU Injection foam are normally injected into cracks that are constantly wet with flowing water.
PU injection resin do not foam when in direct contact with water (non-reactive to water). It is usedfor permanent water-tight sealing with some flexibility to absorb limited movement, in dry or damp cracks and joints. It is not suitable to be injected into cracks that are constantly wet with flowing water.
For more information, please consult Sika’s Technical Service Department.